MORPHOLOGICAL STUDY ON IRRADIATED SAND AND ACTIVATED CARBON

Abstract

Abstract

Sand and activated carbon materials are frequently used in water filtration system. In fact, these common materials take a longer time to filter the water. As this study, to increase the effectiveness of filter materials, both materials were irradiated with neutron and gamma to induce the defect of materials. Early investigation was run by using scanning electron microscope to observe the morphology of materials. It is found that the irradiated sand with neutron shows number of pores with average pore diameter is 1.043μm compared to non-irradiated is 1.334 μm. Irradiated activated carbon with neutron and gamma shows increasing number of pores compared to non-irradiated and have average pore diameter is 0.7881μm and 1.429 μm respectively.

Abstrak

Sistem penapis air kebiasaannya menggunakan bahan seperti pasir dan karbon teraktif. Pada realitinya, kedua-dua bahan ini mengambil masa yang lama untuk menapis air. Kajian ini berperanan untuk memastikan penapisan air menggunakan bahan ini menjadi lebih efektif apabila didedahkan kepada sinaran neutron dan gamma. Kajian awal telah dijalankan dengan menggunakan mikroskop electron pengimbas untuk melihat struktur permukaan bahan yang telah rosak akinat terdedah kepada sinaran radiasi. Hasilnya, pasir yang telah didedahkan dengan radiasi neutron menunjukkan beberapa pori di permukaan dengan purata diameter pori adalah 1.043μm berbanding dengan pasir yang tidak didedahkan kepada radiasi adalah 1.334 μm. Karbon diaktif yang telah terdedah dengan sinaran neutron dan gamma pula menunjukkan peningkatan bilangan pori berbanding dengan karbon teraktif yang tidak terdedah dengan sinaran radiasi dengan masing-masing mempunyai purata diameter pori adalah 0.7881μm dan 1.429 μm